Selectarc INOX 16-8-2B Electrode
This is a simple product
Please contact us for further inquiries including product variety, replacement parts and product details.Description
| Classification | Weld metal composition (%) | Characteristics and applications | Mechanical properties | ø x L (mm) | Parameters | |||
| AWS A5.4 | C | 0.05 | Austenitic stainless steel electrode, basic type coating with approx. 5% ferrite and increased carbon contend. Stable arc, good slag removal, regular weld bead. Good behavior in positional welding and on bad prepared joints. Excellent mechanical properties. Used on 18/8 stainless steels (304H type) and 17-12-2 stainless steels (316H type) as well as for stabilized grades, applied for elevated service temperatures up to +750°C. For petrochemical industry: tubes, heat exchangers, piping systems | Rm (MPa) | >560 | 2.5 x 300 | 70 A | = + |
| E16 8 2-15 | Mn | 1.8 | Rp0,2 (MPa) | >380 | 3.2 x 350 | 90 A | ||
| EN 1600 | Si | 0.4 | A5(%) | >35 | 4.0 x 350 | 120 A | ||
| ISO 3581-A | Ni | 9.0 | KV(J) | +20°C -> >60 | ||||
| E 16 8 2 B 4 3 | Cr | 16.0 | ||||||
| Mo | 1.7 | |||||||
| Fe | Rem. | |||||||
Enquiry about Selectarc INOX 16-8-2B Electrode
Description
| Classification | Weld metal composition (%) | Characteristics and applications | Mechanical properties | ø x L (mm) | Parameters | |||
| AWS A5.4 | C | 0.05 | Austenitic stainless steel electrode, basic type coating with approx. 5% ferrite and increased carbon contend. Stable arc, good slag removal, regular weld bead. Good behavior in positional welding and on bad prepared joints. Excellent mechanical properties. Used on 18/8 stainless steels (304H type) and 17-12-2 stainless steels (316H type) as well as for stabilized grades, applied for elevated service temperatures up to +750°C. For petrochemical industry: tubes, heat exchangers, piping systems | Rm (MPa) | >560 | 2.5 x 300 | 70 A | = + |
| E16 8 2-15 | Mn | 1.8 | Rp0,2 (MPa) | >380 | 3.2 x 350 | 90 A | ||
| EN 1600 | Si | 0.4 | A5(%) | >35 | 4.0 x 350 | 120 A | ||
| ISO 3581-A | Ni | 9.0 | KV(J) | +20°C -> >60 | ||||
| E 16 8 2 B 4 3 | Cr | 16.0 | ||||||
| Mo | 1.7 | |||||||
| Fe | Rem. | |||||||