Elga ELGAMATIC 135 MIG Wire
ELGAMATIC 135 is a copper coated wire for use with the MIG/MAG process, which deposits a 1.5% Ni / 0.3% Mo / 0.2% Cr weld metal. It is intended for welding the high tensile quenched and tempered steels such as Weldox 700, BSC RQT 701, N-A-XTRA 70 and USS T1. ELGAMATIC 135 can be welded with either an Ar/20% CO2 or CO2 gas shield, but the Ar mixture gives better fracture toughness at low temperature and higher strength levels.
Please contact us for further inquiries including product variety, replacement parts and product details.Description
ELGAMATIC 135 is a copper coated wire for use with the MIG/MAG process, which deposits a 1.5% Ni / 0.3% Mo / 0.2% Cr weld metal. It is intended for welding the high tensile quenched and tempered steels such as Weldox 700, BSC RQT 701, N-A-XTRA 70 and USS T1. ELGAMATIC 135 can be welded with either an Ar/20% CO2 or CO2 gas shield, but the Ar mixture gives better fracture toughness at low temperature and higher strength levels.
Classifications
| EN ISO 16834-A | G 69 4 M21 Mn3Ni1CrMo |
|---|---|
| AWS A5.28 | ER100S-G |
Welding Current
DC+
Mechanical Properties
| Yield strength, Re | 725 MPa |
|---|---|
| Tensile strength, Rm | 810 MPa |
| Elongation, A5 | 20% |
| Impact energy, CV | –40°C · 55 J |
Enquiry about Elga ELGAMATIC 135 MIG Wire
Description
ELGAMATIC 135 is a copper coated wire for use with the MIG/MAG process, which deposits a 1.5% Ni / 0.3% Mo / 0.2% Cr weld metal. It is intended for welding the high tensile quenched and tempered steels such as Weldox 700, BSC RQT 701, N-A-XTRA 70 and USS T1. ELGAMATIC 135 can be welded with either an Ar/20% CO2 or CO2 gas shield, but the Ar mixture gives better fracture toughness at low temperature and higher strength levels.
Classifications
| EN ISO 16834-A | G 69 4 M21 Mn3Ni1CrMo |
|---|---|
| AWS A5.28 | ER100S-G |
Welding Current
DC+
Mechanical Properties
| Yield strength, Re | 725 MPa |
|---|---|
| Tensile strength, Rm | 810 MPa |
| Elongation, A5 | 20% |
| Impact energy, CV | –40°C · 55 J |